Product Details:
Usage/Application | Automobile Industry |
Thickness | 0.05-150 mm |
Brand | Jindal |
Width | 1000-2000 mm |
Country of Origin | Made in India |
Length | 2500-6000 mm |
Rahul cutters and slitters is a renowned manufacturer and exporter of SS 304 Coils. We supply SS 304 Coils of different shapes and sizes and with different specifications as per the customers requirements. Our organisation is involved in manufacturing, exporting and trading an extensive range of stainless steel sheets and plates to our clients. Used in various industrial applications, these plates are manufactured by the experienced professionals from high-quality raw material and advanced technology.
The Following Grades Are Available:
Chemical Composition:
SS | 304 |
Ni | 8 – 11 |
Fe | Balance |
Cr | 18 – 20 |
C | 0.08 max |
Si | 0.75 max |
Mn | 2 max |
P | 0.040 max |
S | 0.030 max |
N | – |
Grade | 304 |
Tensile Strength (MPa) min | 515 |
Yield Strength 0.2% Proof (MPa) min | 205 |
Elongation (% in 50mm) min | 40 |
Hardness | |
Rockwell B (HR B) max | 92 |
Brinell (HB) max | 201 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
304 | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
304 | min.max. | –0.08 | –2.0 | –0.75 | –0.045 | –0.030 | 18.020.0 | – | 8.010.5 | –0.10 |
304L | min.max. | –0.030 | –2.0 | –0.75 | –0.045 | –0.030 | 18.020.0 | – | 8.012.0 | –0.10 |
304H | min.max. | 0.040.10 | –2.0 | –0.75 | -0.045 | –0.030 | 18.020.0 | – | 8.010.5 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
304 | 515 | 205 | 40 | 92 | 201 |
304L | 485 | 170 | 40 | 92 | 201 |
304H | 515 | 205 | 40 | 92 | 201 |
304H also has a requirement for a grain size of ASTM No 7 or coarser. |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
304/L/H | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
310 | min.max. | –0.25 | –2.00 | –1.50 | –0.045 | –0.030 | 24.026.0 | – | 19.022.0 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) | ||||
310 | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion(μm/m/°C) | Thermal Conductivity(W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
310 | 7750 | 200 | 15.9 | 16.2 | 17.0 | 14.2 | 18.7 | 500 | 720 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
SS | 316 |
Ni | 10 – 14 |
N | 0.10 max |
Cr | 16 – 18 |
C | 0.08 max |
Si | 0.75 max |
Mn | 2 max |
P | 0.045 max |
S | 0.030 max |
Mo | 2.00 – 3.00 |
Grade | 316 |
Tensile Strength (MPa) min | 515 |
Yield Strength 0.2% Proof (MPa) min | 205 |
Elongation (% in 50mm) min | 40 |
Hardness | |
Rockwell B (HR B) max | 95 |
Brinell (HB) max | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316 | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316L | Min | – | – | – | – | – | 16.0 | 2.00 | 10.0 | – |
Max | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 |
Grade | Tensile Str | Yield Str | Elong | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316L | 485 | 170 | 40 | 95 | 217 |
Grade | Density | Elastic Modulus | Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity | Specific Heat 0-100°C | Elec Resistivity | |||
0-100°C | 0-315°C | 0-538°C | At 100°C | At 500°C | |||||
316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other | |
321 | min.max | –0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.019.0 | – | 9.012.0 | 0.10 | Ti=5(C+N)0.70 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
321 | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
321 | 8027 | 193 | 16.6 | 17.2 | 18.6 | 16.1 | 22.2 | 500 | 720 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Ni | |
410 | min.max. | –0.15 | –1 | –1 | –0.04 | –0.03 | 11.513.5 | 0.75 |
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 480 min | 275 min | 16 min | – | – |
204 | 1475 | 1005 | 11 | 400 | 30 |
316 | 1470 | 961 | 18 | 400 | 36 |
427 | 1340 | 920 | 18.5 | 405 | # |
538 | 985 | 730 | 16 | 321 | # |
593 | 870 | 675 | 20 | 255 | 39 |
650 | 300 | 270 | 29.5 | 225 | 80 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
410 | 7800 | 200 | 9.9 | 11 | 11.5 | 24.9 | 28.7 | 460 | 570 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | |
420 | min.max. | 0.15– | –1 | –1 | –0.040 | –0.03 | 12.014.0 |
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 655 | 345 | 25 | 241 max | – |
204 | 1600 | 1360 | 12 | 444 | 20 |
316 | 1580 | 1365 | 14 | 444 | 19 |
427 | 1620 | 1420 | 10 | 461 | # |
538 | 1305 | 1095 | 15 | 375 | # |
593 | 1035 | 810 | 18 | 302 | 22 |
650 | 895 | 680 | 20 | 262 | 42 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
420 | 7800 | 200 | 10.3 | 10.8 | 11.7 | 24.9 | – | 460 | 550 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | |
420 | min.max. | 0.15– | –1 | –1 | –0.040 | –0.03 | 12.014.0 |
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 655 | 345 | 25 | 241 max | – |
204 | 1600 | 1360 | 12 | 444 | 20 |
316 | 1580 | 1365 | 14 | 444 | 19 |
427 | 1620 | 1420 | 10 | 461 | # |
538 | 1305 | 1095 | 15 | 375 | # |
593 | 1035 | 810 | 18 | 302 | 22 |
650 | 895 | 680 | 20 | 262 | 42 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
420 | 7800 | 200 | 10.3 | 10.8 | 11.7 | 24.9 | – | 460 | 550 |
Product Details:
Width | 1000-2000 mm |
Thickness | 0.05-150 mm |
Length | 2500-6000 mm |
GradeN | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
430 | min.max. | –0.12 | –1 | –1 | –0.04 | –0.030 | 1618 | – | –0.50 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
430 | 483 | 310 | 22 | 85 | 183 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
430 | 7750 | 200 | 10.4 | 11.0 | 11.4 | 26.1 | 26.3 | 460 | 600 |