Product Details:
Material | ss |
Grade | ss 310 |
Country of Origin | Made in India |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Thickness | 0.05-150 mm |
Grade | C | Mn | Si | P |
| Cr | Mo | Ni | N | |
310 | min.max. | –0.25 | –2.00 | –1.50 | –0.045 | –0.030 | 24.026.0 | – | 19.022.0 | – |
Mechanical Properties:
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) | ||||
310 | 515 | 205 | 40 | 95 | 217 |
Physical Properties:
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion(μm/m/°C) | Thermal Conductivity(W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
310 | 7750 | 200 | 15.9 | 16.2 | 17.0 | 14.2 | 18.7 | 500 | 720 |
Product Details:
Steel Grade | SS 304, SS304 L |
Standard | ASTM |
Surface Treatment | Hot Rolled |
Is It Rust Proof | Rust Proof |
Material | Stainless Steel |
Product Details:
Steel Grade | SS 301 |
Thickness | 2-3 mm |
Surface Treatment | Hot Rolled |
Shape | Rectangular |
Usage/Application | Construction |
Standard | ASTM |
Country of Origin | Made in India |
Product Details:
Steel Grade | SS 309 |
Thickness | 1-2 mm |
Surface Treatment | Hot Rolled |
Shape | Rectangular |
Country of Origin | Made in India |
Material | Stainless Steel |
Product Details:
Steel Grade | SS 420 |
Thickness | 2-3 mm |
Surface Treatment | Hot Rolled |
Shape | Rectangular |
Usage/Application | Industrial |
Country of Origin | Made in India |
Product Details:
Thickness | 1-2 mm |
Steel Grade | SS 409, SS 409M |
Surface Treatment | Hot Rolled |
Shape | Rectangular |
Usage/Application | Industrial |
Standard | ASTM |
Country of Origin | Made in India |
Product Details:
Thickness | 1-2 mm |
Steel Grade | SS 904,SS 904L |
Surface Treatment | Hot Rolled |
Shape | Rectangular |
Usage/Application | Construction |
Country of Origin | Made in India |
Product Details:
Grade | ss 310 |
Material Grade | SS 310, SS 310S |
Thickness | 2 mm |
Surface Treatment | Hot Rolled |
Country of Origin | Made in India |
Material | Stainless Steel |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-600 mm |
Chemical Composition:
SS | 304 |
Ni | 8 – 11 |
Fe | Balance |
Cr | 18 – 20 |
C | 0.08 max |
Si | 0.75 max |
Mn | 2 max |
P | 0.040 max |
S | 0.030 max |
N | – |
Grade | 304 |
Tensile Strength (MPa) min | 515 |
Yield Strength 0.2% Proof (MPa) min | 205 |
Elongation (% in 50mm) min | 40 |
Hardness | |
Rockwell B (HR B) max | 92 |
Brinell (HB) max | 201 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
304 | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Ni | |
410 | min.max. | –0.15 | –1 | –1 | –0.04 | –0.03 | 11.513.5 | 0.75 |
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 480 min | 275 min | 16 min | – | – |
204 | 1475 | 1005 | 11 | 400 | 30 |
316 | 1470 | 961 | 18 | 400 | 36 |
427 | 1340 | 920 | 18.5 | 405 | # |
538 | 985 | 730 | 16 | 321 | # |
593 | 870 | 675 | 20 | 255 | 39 |
650 | 300 | 270 | 29.5 | 225 | 80 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
410 | 7800 | 200 | 9.9 | 11 | 11.5 | 24.9 | 28.7 | 460 | 570 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P |
| Cr | Mo | Ni | N | Other | |
321 | min.max | –0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.019.0 | – | 9.012.0 | 0.10 | Ti=5(C+N)0.70 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
321 | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
321 | 8027 | 193 | 16.6 | 17.2 | 18.6 | 16.1 | 22.2 | 500 | 720 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
304 | min.max. | –0.08 | –2.0 | –0.75 | –0.045 | –0.030 | 18.020.0 | – | 8.010.5 | –0.10 |
304L | min.max. | –0.030 | –2.0 | –0.75 | –0.045 | –0.030 | 18.020.0 | – | 8.012.0 | –0.10 |
304H | min.max. | 0.040.10 | –2.0 | –0.75 | -0.045 | –0.030 | 18.020.0 | – | 8.010.5 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
304 | 515 | 205 | 40 | 92 | 201 |
304L | 485 | 170 | 40 | 92 | 201 |
304H | 515 | 205 | 40 | 92 | 201 |
304H also has a requirement for a grain size of ASTM No 7 or coarser. |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
304/L/H | 8000 | 193 | 17.2 | 17.8 | 18.4 | 16.2 | 21.5 | 500 | 720 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | |
420 | min.max. | 0.15– | –1 | –1 | –0.040 | –0.03 | 12.014.0 |
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 655 | 345 | 25 | 241 max | – |
204 | 1600 | 1360 | 12 | 444 | 20 |
316 | 1580 | 1365 | 14 | 444 | 19 |
427 | 1620 | 1420 | 10 | 461 | # |
538 | 1305 | 1095 | 15 | 375 | # |
593 | 1035 | 810 | 18 | 302 | 22 |
650 | 895 | 680 | 20 | 262 | 42 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
420 | 7800 | 200 | 10.3 | 10.8 | 11.7 | 24.9 | – | 460 | 550 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | |
420 | min.max. | 0.15– | –1 | –1 | –0.040 | –0.03 | 12.014.0 |
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength | Elongation (% in 50mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
Annealed * | 655 | 345 | 25 | 241 max | – |
204 | 1600 | 1360 | 12 | 444 | 20 |
316 | 1580 | 1365 | 14 | 444 | 19 |
427 | 1620 | 1420 | 10 | 461 | # |
538 | 1305 | 1095 | 15 | 375 | # |
593 | 1035 | 810 | 18 | 302 | 22 |
650 | 895 | 680 | 20 | 262 | 42 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
420 | 7800 | 200 | 10.3 | 10.8 | 11.7 | 24.9 | – | 460 | 550 |
Product Details:
Steel Grade | SS 301LN |
Standard | ASTM |
Surface Treatment | Hot Rolled |
Shape | Rectangular |
Product Details:
Steel Grade | SS 316, SS 316L |
Surface Treatment | Hot Rolled |
Material | Stainless Steel |
Product Details:
Material | Stainless Steel |
Material Grade | SS 410, SS 410S |
Shape | Rectangular |
Product Details:
Thickness | 0.5-150 mm |
Shape | Rectangular |
Material | Stainless Steel |
Product Details:
Type | Plate |
Steel Grade | SS316 L |
Thickness | 0.05-150 mm |
Country of Origin | Made in India |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
SS | 316 |
Ni | 10 – 14 |
N | 0.10 max |
Cr | 16 – 18 |
C | 0.08 max |
Si | 0.75 max |
Mn | 2 max |
P | 0.045 max |
S | 0.030 max |
Mo | 2.00 – 3.00 |
Grade | 316 |
Tensile Strength (MPa) min | 515 |
Yield Strength 0.2% Proof (MPa) min | 205 |
Elongation (% in 50mm) min | 40 |
Hardness | |
Rockwell B (HR B) max | 95 |
Brinell (HB) max | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316 | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Thickness | 0.05-150 mm |
Steel Grade | SS 304 |
Material | ss |
Length | 2500-6000 mm |
Country of Origin | Made in India |
Width | 1000-2000 mm |
GradeN | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
430 | min.max. | –0.12 | –1 | –1 | –0.04 | –0.030 | 1618 | – | –0.50 | – |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
430 | 483 | 310 | 22 | 85 | 183 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
430 | 7750 | 200 | 10.4 | 11.0 | 11.4 | 26.1 | 26.3 | 460 | 600 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316L | Min | – | – | – | – | – | 16.0 | 2.00 | 10.0 | – |
Max | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 |
Grade | Tensile Str | Yield Str | Elong | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316L | 485 | 170 | 40 | 95 | 217 |
Grade | Density | Elastic Modulus | Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity | Specific Heat 0-100°C | Elec Resistivity | |||
0-100°C | 0-315°C | 0-538°C | At 100°C | At 500°C | |||||
316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Product Details:
Thickness | 0.05-150 mm |
Width | 1000-2000 mm |
Length | 2500-6000 mm |
Grade | C | Mn | Si | P |
| Cr | Mo | Ni | N | Other | |
321 | min.max | –0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.019.0 | – | 9.012.0 | 0.10 | Ti=5(C+N)0.70 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
321 | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
321 | 8027 | 193 | 16.6 | 17.2 | 18.6 | 16.1 | 22.2 | 500 | 720 |